KAJIAN KONSENTRASI DAN RASIO GELATIN DARI KULIT IKAN PATIN DAN KAPPA KARAGENAN PADA PEMBUATAN JELI

Eveline ., Joko Santoso, Ivan Widjaja

Abstract

Jelly is a dessert that requires gelling agent on the making process. Besides kappa carrageenan originated from Eucheuma cottonii, the gelatin obtained from  catfish skin was also  used as the alternative source of gelling agent The purpose of this research  was to obtain the best concentration and  ratio of patin fish gelatin and kappa carrageenan in jelly formulation, and to study the physical and sensory characteristics of the modified jelly.. The formulation of jellies were combination of  concentration and gelling agent ratio (gelatin:kappa  carrageenan), which are 1%, 1:1; 1%, 2:1; 1%, 1:2; 2%, 1:1; 2%, 2:1; 2%, 1:2; 3%, 1:1; 3%, 2:1; and 3%, 1:2 respectively. The best combination was determined based on the best score obtained from each test parameters on physical and sensory analyses. The result showed that concentration and gelling agent ratio affect physical and sensory characterstics of the jelly. Jelly with 2% gelling agent and gelatin : kappa carrageenan ratio of 2:1 was the best formula which possessed the closest physical characteristic to the commercial jelly (not significantly different) on gel strength parameter (123.29 g cm) and viscosity (79.90 cPs); although gelling point (32.83 °C), melting point (45.83 °C), pH (5.20), and syneresis degree (0.07%) were significantly different. The best jelly had better syneresis degree compared to the commercial one (lower numeric score). For the sensory characteristic, the best jelly was still less in (chewiness), color (clarity), and overall acceptance.

Key words: Eucheuma cottonii, gelatin, jelly, kappa carragenan, patin fish

Authors

Eveline .
jphpi@ipb.ac.id (Primary Contact)
Joko Santoso
Ivan Widjaja
.E., SantosoJ., & WidjajaI. (1). KAJIAN KONSENTRASI DAN RASIO GELATIN DARI KULIT IKAN PATIN DAN KAPPA KARAGENAN PADA PEMBUATAN JELI. Jurnal Pengolahan Hasil Perikanan Indonesia, 14(2). https://doi.org/10.17844/jphpi.v14i2.5318

Article Details