PENGUJIAN SIFAT FISIS-MEKANIS DAN NONDESTRUKTIF METODE GELOMBANG SUARA PAPAN WOL SEMEN BERKERAPATAN SEDANG-TINGGI BAMBU BETUNG (DENDROCALAMUS ASPER)

  • Lina Karlinasari
  • Dede Hermawan
  • Akhiruddin Maddu
  • M. Farouq Iksan
  • Anita Firmanti
Keywords: Betung bamboo, nondestructive testing, physical-mechanical properties, stress wave velocity, wool cement board

Abstract

Cement board is a composite wood product has advantages such as fire resistance, termite, water resistant, and has good sound insulation properties. Bamboo is suitable material that can be used as a raw material of cement board. The objectove of this study was to determine the physical-mechanical properties of wool cement boards from betung bamboo (Dendrocalamus asper) in various densities. Mechanical testing included nondestructive testing performed using the sound waves velocity method (stress wave velocity). The material used was particles of wool/ excelsior dimensions. The adhesive used was Portland cement type I by the ratio of bamboo: cement: water 1:2:1. Target board densities were 0.5 g/cm3; 0.8 g/cm3; and 1.0 g/cm3. The results showed the higher density of the board the higher mechanical properties of boards. The difference density cement board was more influential on mechanical properties (MOE, MOR, SW) board compared with those physical properties. Nondestrcutive testing using sound waves velocity method can be used to predict mechanical bending properties of wool cement board of betung bamboo as indicated by the close relationship between the parameter estimators (dynamic MOE) and static testing value (MOE and MOR).

 

Downloads

Download data is not yet available.

Author Biographies

Lina Karlinasari
Departemen Hasil Hutan, Fakultas Kehutanan, Institut Pertanian Bogor. Kampus IPB Darmaga Bogor 16001
Dede Hermawan
Departemen Hasil Hutan, Fakultas Kehutanan, Institut Pertanian Bogor. Kampus IPB Darmaga Bogor 16001
Akhiruddin Maddu
Departemen Fisika, Fakultas Matematika dan IPA, Institut Pertanian Bogor. Kampus IPB Darmaga Bogor 16001
M. Farouq Iksan
Departemen Hasil Hutan, Fakultas Kehutanan, Institut Pertanian Bogor. Kampus IPB Darmaga Bogor 16001
Anita Firmanti
Pusat Penelitian Pemukiman, Balitbang Kementerian PU, Jl. Panyaungan, Cileunyi, Bandung

References

Badejo S.O.J. 1998. Effect of flake geometry on properties of cement-bonded particleboar from mixed tropical hardwoods. Wood Sci. Technol. 22, 357-370.

de Souza M.R., R.L. Geimer, dan A.A. Moslemi. 1997. Degradation of conventional and CO2-injected cement-bonded particleboard by exposure to fungi and termite. Journal of Tropical Products 3(1): 63-69.

Frybort S., R. Mauritz, A. Teischinger, dan U. Muller. 2008. Cement bonded composite – A mechanical review. BioResources 3 (2): 602-626.

Han, G., Q. Wu, dan X. Wang. 2006. Stress-wave velocity of wood-based panels: Effect of mositure, product type, and material direction. Forest Products Journal Vol 56 (1): 28-33.

Hermawan D. 2001. Manufacture of cement-bonded particleboard using carbon dioxide curing technology. [Ph.D. Disertasi]. Department of Forest and Biomass Science, Graduate School of The Faculty of Agriculture Kyoto University.

[JSA] Japanese Standard Association. 1992. Cement bonded particleboards. Japanese Industrial Standard (JIS) A 5417-1992. Japan.

Karlinasari L, S. Surjokusumo, Y.S. Hadi, dan N. Nugroho. 2005. Non destructive testing on six tropical woods using utrasonic method. Dalam Prosiding: 6th International Wood Science Symposium. 28-30 Agustus 2005. Bali. Indonesia.

Karlinasari L. 2007. Analisis kekakuan kayu berdasarkan pengujian nondestruktif metode gelombang ultrasonik dan kekuatan lentur kayu berdasarkan pengujian destruktif. [Disertasi]. Program Pascasarjana, Institut Pertanian Bogor.

Karlinasari L, M.E. Wahyuna, dan N. Nugroho. 2008. Non-destructive ultrasonic testing method for determining bending strength properties of gmelina wood (Gmelina arborea Roxb.). Journal of Tropical Forest Science 20(2): 99-104.

Karlinasari, L., M..F. Ikhsan, D. Hermawan, dan A. Maddu. 2011. Pengujian nondestruktif metode gelombang suara pada papan partikel semen. Makalah lengkap pada Seminar Nasional Masyarakat Penelitian Kayu Indonesia (MAPEKI) XIV, 2 November 2011 Yogyakarta, Indonesia.

Ma L.F. 2010. Manufacture of bamboo-cemnet particleboard. http://www.inbar.int/econodevep/proceeding/Pa-Ma-Manufacture%20of% (diunduh 14 April 2010)

Maail R S., D. Hermawan, dan Y.S. Hadi. 2006. Pembuatan papan semen-gypsum dari core-kenaf (Hibiscus cannabinus L.) menggunakan teknologi pengerasan autoclave. Jurnal Teknologi Hasil Hutan 19(1): 55-66.

Shigekura Y. K. Takahashi, K. Koga, dan M. Funasaki. 1992. Properties of wood fiber-cement composite materials manufactures by an extruder. Dalam prosiding: 3th International inorganic-bonded wood and fiber composite materials. Sponake, Washington, USA. Hal 42-47.

Sulastiningsih I.M., P. Sutigno, dan Y.H. Priyadi. 1999. The properties of cement-bonded boards from sengon wood. Buletin Penelitian Hasil Hutan. Vol 16 (5): 279-286.

Sulastiningsih I.M., N. Hadjib, S. Murdjoko, dan S. Kawai. 2000. The effect of bamboo:cement ratio and magnesium chloride (MgCl2) content on the properties of bamboo-cement boards. Dalam prosiding: Wood-cement composites in the Asia-Pacific Region. 10 December 2000. Canbera, Australia.

Published
2012-05-05
How to Cite
KarlinasariL., HermawanD., MadduA., IksanM. F., & FirmantiA. (2012). PENGUJIAN SIFAT FISIS-MEKANIS DAN NONDESTRUKTIF METODE GELOMBANG SUARA PAPAN WOL SEMEN BERKERAPATAN SEDANG-TINGGI BAMBU BETUNG (DENDROCALAMUS ASPER). Jurnal Ilmu Pertanian Indonesia, 17(1), 16-21. Retrieved from https://jurnal.ipb.ac.id/index.php/JIPI/article/view/8033

Most read articles by the same author(s)